What are the appropriate applications for 16MnCr5 and Q355B? Can both achieve a carburizing strength of 58-62 HRC?

● 2025-11-05 ● - ● Leave me a message
A:Q355 can be achieved through optimized heat treatment processes.
Material Surface Hardness (HRC) Core Hardness (HRC) Hardened Layer Depth (mm) Suitability
16MnCr5 58-62 28-35 0.8-1.5 Heavy-duty gears, transmission shafts
Q355B 40-45 (optimized ≤50) <20 0.3-0.6 (non-uniform)

Previous:

What material is used for the inner frame of the paving bricks? Is it 16MnCr5 (German board) or Q355B (domestic board)? Can both achieve a carburizing strength of 58-62 HRC? According to information found on Chatgpt, the former can achieve a carburizing strength of 58-62 HRC, but the latter is around 55-60 HRC. If a customer inquires, it will cause distrust and doubt.

Next:

How much does nitriding treatment on mold surfaces improve wear resistance? Can this be quantified?

Send Inquiry


X
We use cookies to offer you a better browsing experience, analyze site traffic and personalize content. By using this site, you agree to our use of cookies. Privacy Policy
Reject Accept